Touch lens产品由Icon,上部ITO film,印刷层,下部ITO film,加上PC等结构组成.
Icon表面可依不同客户需求印刷或溅镀不同颜色或图面已增加质感与美观性.
除一般Iocn/F/F/PC产品外,接口光电也同时拥有不同结构的Touch lens制造技术. 如Icon/F/F/Glass, Icon/F/ITO glass,Icon/F/ITO glass(PC)等.
|
| |
光学规格
|
TP Structure
|
Film Surface Treatment
|
Specification
|
|
Icon/F/F/PC
|
Clear+Clear
|
Min. 77%, Typical 79%
|
|
Icon/F/F/PC
|
Clear+AG
|
Min. 75%, Typical 77%
|
|
Icon/F/F/G
|
Clear+Clear
|
Min. 77%, Typical 79%
|
|
Icon/F/F/G
|
Clear+AG
|
Min. 75%, Typical 77%
|
|
Icon/F/G
|
Clear
|
Min. 79%, Typical 81%
|
|
Icon/F/G
|
AG
|
Min. 77%, Typical 79%
|
入力/硬度/FPC拉力规格
| Description |
Spec. |
Remark |
| Input Method |
Finger or Pen |
|
| Activation Force |
50 gf |
From VA 35mm |
| Hardness of surface |
3H |
JIS K 5400 |
| FPC Peeling Force |
Minimum 500 gf/cm |
Pull upward by 90o↑ |
| FPC Bending Resistance |
Meet electrical spec. after testing |
Bending degree: 180o |
| Bending radius: R1 mm |
| Bending times : 30 times |
Durability规格
|
Description
|
Spec.
|
Remark
|
|
Pen Sliding
Durability
|
>105 Times
|
Test Condition:
|
|
End shape:R0.8 mm
|
|
Material of Pen: Poly-acetal resin
|
|
Load force: 250 gf
|
|
Sliding length: 35 mm
|
|
Writing speed: 300 mm/sec.
|
|
Pen Pitting
Durability
|
>106 times
|
End shape:R0.8mm
|
|
Material of Pen: Poly-acetal resin
|
|
Load force: 250 gf
|
|
Frequency: 5 Hz
|
|
By PA stylus tapping at same points
|
|
Finger knocking Durability
|
>106 times
|
End shape:R8mm, Hardness:50-600
|
|
Load force: 250 gf
|
|
Frequency: 5 Hz
|
|
By Silicon rubber tapping at same points
|
Reliability
High temperature test:
70 ℃, 240 hrs
Low temperature test:
-20 ℃, 240 hrs
High Temp/High Humid. Test:
60 ℃ / 90%RH, 240 hrs
Thermal shock Test:
-30℃(0.5H)→ 70℃(0.5H),Total 20 cycles
Environmental Condition
Storage (-20℃ ~ 70℃ )
Temperature -20 °C ~ +60 °C, humidity 10% ~ 90%.
Temperature +60 °C ~ +70 °C, humidity 10% ~ 60%.
Non-Condensing.
Operate (-10℃ ~ 60℃ )
Temperature -10 °C ~ +40 °C, humidity 10% ~ 90%.
Temperature +40 °C ~ +60 °C, humidity 10% ~ 60%.
Non-Condensing. |
首页 >
Touch Lens > Touch Lens 